EN 1.4482 Stainless Steel vs. EN-MC21310 Magnesium
EN 1.4482 stainless steel belongs to the iron alloys classification, while EN-MC21310 magnesium belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.4482 stainless steel and the bottom bar is EN-MC21310 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 45 |
| Elongation at Break, % | 34 | |
| 9.0 |
| Fatigue Strength, MPa | 420 to 450 | |
| 86 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 17 |
| Shear Strength, MPa | 510 to 530 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 800 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 530 to 570 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 360 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 100 |
| Melting Completion (Liquidus), °C | 1420 | |
| 600 |
| Melting Onset (Solidus), °C | 1370 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 1000 |
| Thermal Conductivity, W/m-K | 15 | |
| 89 |
| Thermal Expansion, µm/m-K | 13 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 12 |
| Density, g/cm3 | 7.7 | |
| 1.6 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 23 |
| Embodied Energy, MJ/kg | 38 | |
| 160 |
| Embodied Water, L/kg | 150 | |
| 970 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 230 to 250 | |
| 16 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 690 to 820 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 73 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 34 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 47 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 55 |
| Thermal Shock Resistance, points | 21 to 22 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 1.8 to 2.6 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 19.5 to 21.5 | |
| 0 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 to 0.010 |
| Iron (Fe), % | 66.1 to 74.9 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 | |
| 95.2 to 97.4 |
| Manganese (Mn), % | 4.0 to 6.0 | |
| 0.1 to 0.7 |
| Molybdenum (Mo), % | 0.1 to 0.6 | |
| 0 |
| Nickel (Ni), % | 1.5 to 3.5 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0.050 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.7 to 1.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.010 |