EN 1.4507 Stainless Steel vs. Grade 200 Maraging Steel

Both EN 1.4507 stainless steel and grade 200 maraging steel are iron alloys. They have 71% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.4507 stainless steel and the bottom bar is grade 200 maraging steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
9.1 to 18
Poisson's Ratio 0.27
0.3
Shear Modulus, GPa 80
74
Shear Strength, MPa 530
600 to 890
Tensile Strength: Ultimate (UTS), MPa 840
970 to 1500
Tensile Strength: Yield (Proof), MPa 590
690 to 1490

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 21
31
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 4.0
4.5
Embodied Energy, MJ/kg 55
59
Embodied Water, L/kg 180
140

Common Calculations

PREN (Pitting Resistance) 41
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 850
1240 to 5740
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 30
33 to 51
Strength to Weight: Bending, points 25
27 to 35
Thermal Shock Resistance, points 23
29 to 45

Alloy Composition

Aluminum (Al), % 0
0.050 to 0.15
Boron (B), % 0
0 to 0.0030
Calcium (Ca), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
0
Cobalt (Co), % 0
8.0 to 9.0
Copper (Cu), % 1.0 to 2.5
0
Iron (Fe), % 56.4 to 65.8
67.8 to 71.8
Manganese (Mn), % 0 to 2.0
0 to 0.1
Molybdenum (Mo), % 3.0 to 4.0
3.0 to 3.5
Nickel (Ni), % 6.0 to 8.0
17 to 19
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 0.7
0 to 0.1
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.020