EN 1.4508 Stainless Steel vs. ACI-ASTM CD3MN Steel

Both EN 1.4508 stainless steel and ACI-ASTM CD3MN steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is ACI-ASTM CD3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
29
Fatigue Strength, MPa 210
340
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
79
Tensile Strength: Ultimate (UTS), MPa 570
710
Tensile Strength: Yield (Proof), MPa 260
460

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 1000
1060
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
18
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
3.6
Embodied Energy, MJ/kg 55
50
Embodied Water, L/kg 160
160

Common Calculations

PREN (Pitting Resistance) 32
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
180
Resilience: Unit (Modulus of Resilience), kJ/m3 170
530
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 4.1
4.3
Thermal Shock Resistance, points 17
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
21 to 23.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 61.2 to 69.9
62.6 to 71.9
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 3.0 to 3.5
2.5 to 3.5
Nickel (Ni), % 9.0 to 12
4.5 to 6.5
Nitrogen (N), % 0.1 to 0.2
0.1 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020