EN 1.4508 Stainless Steel vs. ASTM A387 Grade 2 Steel

Both EN 1.4508 stainless steel and ASTM A387 grade 2 steel are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is ASTM A387 grade 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
25
Fatigue Strength, MPa 210
190 to 250
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 570
470 to 550
Tensile Strength: Yield (Proof), MPa 260
260 to 350

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
420
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.6
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.6
Embodied Energy, MJ/kg 55
20
Embodied Water, L/kg 160
50

Common Calculations

PREN (Pitting Resistance) 32
2.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
98 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 170
180 to 320
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
16 to 20
Strength to Weight: Bending, points 19
17 to 19
Thermal Diffusivity, mm2/s 4.1
12
Thermal Shock Resistance, points 17
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.030
0.050 to 0.21
Chromium (Cr), % 18 to 20
0.5 to 0.8
Iron (Fe), % 61.2 to 69.9
97.1 to 98.3
Manganese (Mn), % 0 to 1.5
0.55 to 0.8
Molybdenum (Mo), % 3.0 to 3.5
0.45 to 0.6
Nickel (Ni), % 9.0 to 12
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
0.15 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.025