EN 1.4508 Stainless Steel vs. EN 1.4404 Stainless Steel

Both EN 1.4508 stainless steel and EN 1.4404 stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is EN 1.4404 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
14 to 43
Fatigue Strength, MPa 210
220 to 320
Impact Strength: V-Notched Charpy, J 90
91 to 93
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 570
600 to 900
Tensile Strength: Yield (Proof), MPa 260
240 to 570

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1000
950
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
3.8
Embodied Energy, MJ/kg 55
52
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 32
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
110 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140 to 800
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21 to 32
Strength to Weight: Bending, points 19
20 to 26
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 17
13 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
16.5 to 18.5
Iron (Fe), % 61.2 to 69.9
62.8 to 71.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
2.0 to 2.5
Nickel (Ni), % 9.0 to 12
10 to 13
Nitrogen (N), % 0.1 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015