EN 1.4508 Stainless Steel vs. EN 1.4833 Stainless Steel

Both EN 1.4508 stainless steel and EN 1.4833 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have a moderately high 93% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is EN 1.4833 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
38
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 570
600
Tensile Strength: Yield (Proof), MPa 260
240

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 1000
1000
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
19
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
3.5
Embodied Energy, MJ/kg 55
50
Embodied Water, L/kg 160
170

Common Calculations

PREN (Pitting Resistance) 32
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
180
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 17
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 18 to 20
22 to 24
Iron (Fe), % 61.2 to 69.9
58.7 to 66
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
12 to 14
Nitrogen (N), % 0.1 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015