EN 1.4508 Stainless Steel vs. EN 1.6563 Steel

Both EN 1.4508 stainless steel and EN 1.6563 steel are iron alloys. They have 69% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is EN 1.6563 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 570
620 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 20
3.6
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
1.7
Embodied Energy, MJ/kg 55
22
Embodied Water, L/kg 160
54

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
22 to 65
Strength to Weight: Bending, points 19
21 to 43
Thermal Diffusivity, mm2/s 4.1
12
Thermal Shock Resistance, points 17
18 to 54

Alloy Composition

Carbon (C), % 0 to 0.030
0.38 to 0.44
Chromium (Cr), % 18 to 20
0.7 to 0.9
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 61.2 to 69.9
94.9 to 96.5
Manganese (Mn), % 0 to 1.5
0.6 to 0.9
Molybdenum (Mo), % 3.0 to 3.5
0.15 to 0.3
Nickel (Ni), % 9.0 to 12
1.7 to 2.0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025