EN 1.4508 Stainless Steel vs. Nickel 686

EN 1.4508 stainless steel belongs to the iron alloys classification, while nickel 686 belongs to the nickel alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is nickel 686.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 34
51
Fatigue Strength, MPa 210
410
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 570
780
Tensile Strength: Yield (Proof), MPa 260
350

Thermal Properties

Latent Heat of Fusion, J/g 300
320
Maximum Temperature: Mechanical, °C 1000
980
Melting Completion (Liquidus), °C 1450
1380
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 15
9.8
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 20
70
Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 4.0
12
Embodied Energy, MJ/kg 55
170
Embodied Water, L/kg 160
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
320
Resilience: Unit (Modulus of Resilience), kJ/m3 170
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 4.1
2.6
Thermal Shock Resistance, points 17
21

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.010
Chromium (Cr), % 18 to 20
19 to 23
Iron (Fe), % 61.2 to 69.9
0 to 5.0
Manganese (Mn), % 0 to 1.5
0 to 0.75
Molybdenum (Mo), % 3.0 to 3.5
15 to 17
Nickel (Ni), % 9.0 to 12
49.5 to 63
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.080
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0.020 to 0.25
Tungsten (W), % 0
3.0 to 4.4