EN 1.4508 Stainless Steel vs. S17400 Stainless Steel

Both EN 1.4508 stainless steel and S17400 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is S17400 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 21
Fatigue Strength, MPa 210
380 to 670
Impact Strength: V-Notched Charpy, J 90
7.6 to 86
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
75
Tensile Strength: Ultimate (UTS), MPa 570
910 to 1390
Tensile Strength: Yield (Proof), MPa 260
580 to 1250

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
450
Maximum Temperature: Mechanical, °C 1000
850
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
14
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
2.7
Embodied Energy, MJ/kg 55
39
Embodied Water, L/kg 160
130

Common Calculations

PREN (Pitting Resistance) 32
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 170
880 to 4060
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
32 to 49
Strength to Weight: Bending, points 19
27 to 35
Thermal Diffusivity, mm2/s 4.1
4.5
Thermal Shock Resistance, points 17
30 to 46

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.070
Chromium (Cr), % 18 to 20
15 to 17
Copper (Cu), % 0
3.0 to 5.0
Iron (Fe), % 61.2 to 69.9
70.4 to 78.9
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
3.0 to 5.0
Niobium (Nb), % 0
0.15 to 0.45
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030