EN 1.4508 Stainless Steel vs. S44401 Stainless Steel

Both EN 1.4508 stainless steel and S44401 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4508 stainless steel and the bottom bar is S44401 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
21
Fatigue Strength, MPa 210
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 570
480
Tensile Strength: Yield (Proof), MPa 260
300

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
510
Maximum Temperature: Mechanical, °C 1000
930
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
22
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
2.9
Embodied Energy, MJ/kg 55
40
Embodied Water, L/kg 160
130

Common Calculations

PREN (Pitting Resistance) 32
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
90
Resilience: Unit (Modulus of Resilience), kJ/m3 170
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 4.1
5.9
Thermal Shock Resistance, points 17
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.025
Chromium (Cr), % 18 to 20
17.5 to 19.5
Iron (Fe), % 61.2 to 69.9
75.1 to 80.6
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
1.8 to 2.5
Nickel (Ni), % 9.0 to 12
0 to 1.0
Nitrogen (N), % 0.1 to 0.2
0 to 0.035
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0.2 to 0.8