EN 1.4509 Stainless Steel vs. AISI 301L Stainless Steel

Both EN 1.4509 stainless steel and AISI 301L stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is AISI 301L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
210 to 320
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
22 to 50
Fatigue Strength, MPa 170
240 to 530
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 330
440 to 660
Tensile Strength: Ultimate (UTS), MPa 530
620 to 1040
Tensile Strength: Yield (Proof), MPa 260
250 to 790

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Maximum Temperature: Corrosion, °C 570
410
Maximum Temperature: Mechanical, °C 890
890
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
13
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
2.7
Embodied Energy, MJ/kg 41
39
Embodied Water, L/kg 120
130

Common Calculations

PREN (Pitting Resistance) 18
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
210 to 300
Resilience: Unit (Modulus of Resilience), kJ/m3 180
160 to 1580
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
22 to 37
Strength to Weight: Bending, points 19
21 to 29
Thermal Diffusivity, mm2/s 6.8
4.1
Thermal Shock Resistance, points 19
14 to 24

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 18.5
16 to 18
Iron (Fe), % 77.8 to 82.1
70.7 to 78
Manganese (Mn), % 0 to 1.0
0 to 2.0
Nickel (Ni), % 0
6.0 to 8.0
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.1 to 0.6
0