EN 1.4509 Stainless Steel vs. AISI 304L Stainless Steel

Both EN 1.4509 stainless steel and AISI 304L stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is AISI 304L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160 to 350
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
6.7 to 46
Fatigue Strength, MPa 170
170 to 430
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 330
370 to 680
Tensile Strength: Ultimate (UTS), MPa 530
540 to 1160
Tensile Strength: Yield (Proof), MPa 260
190 to 870

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 570
420
Maximum Temperature: Mechanical, °C 890
540
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
16
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
3.1
Embodied Energy, MJ/kg 41
44
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 18
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
71 to 240
Resilience: Unit (Modulus of Resilience), kJ/m3 180
92 to 1900
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
19 to 41
Strength to Weight: Bending, points 19
19 to 31
Thermal Diffusivity, mm2/s 6.8
4.2
Thermal Shock Resistance, points 19
12 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 18.5
18 to 20
Iron (Fe), % 77.8 to 82.1
65 to 74
Manganese (Mn), % 0 to 1.0
0 to 2.0
Nickel (Ni), % 0
8.0 to 12
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.1 to 0.6
0