EN 1.4509 Stainless Steel vs. EN 1.4606 Stainless Steel

Both EN 1.4509 stainless steel and EN 1.4606 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is EN 1.4606 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
23 to 39
Fatigue Strength, MPa 170
240 to 420
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
75
Shear Strength, MPa 330
410 to 640
Tensile Strength: Ultimate (UTS), MPa 530
600 to 1020
Tensile Strength: Yield (Proof), MPa 260
280 to 630

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 570
770
Maximum Temperature: Mechanical, °C 890
910
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
14
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
26
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
6.0
Embodied Energy, MJ/kg 41
87
Embodied Water, L/kg 120
170

Common Calculations

PREN (Pitting Resistance) 18
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
190 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 180
200 to 1010
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
21 to 36
Strength to Weight: Bending, points 19
20 to 28
Thermal Diffusivity, mm2/s 6.8
3.7
Thermal Shock Resistance, points 19
21 to 35

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 17.5 to 18.5
13 to 16
Iron (Fe), % 77.8 to 82.1
49.2 to 59
Manganese (Mn), % 0 to 1.0
1.0 to 2.0
Molybdenum (Mo), % 0
1.0 to 1.5
Nickel (Ni), % 0
24 to 27
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0.1 to 0.6
1.9 to 2.3
Vanadium (V), % 0
0.1 to 0.5