EN 1.4509 Stainless Steel vs. EN 1.4919 Stainless Steel

Both EN 1.4509 stainless steel and EN 1.4919 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
40
Fatigue Strength, MPa 170
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 330
400
Tensile Strength: Ultimate (UTS), MPa 530
590
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 570
410
Maximum Temperature: Mechanical, °C 890
950
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
16
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
19
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
3.8
Embodied Energy, MJ/kg 41
52
Embodied Water, L/kg 120
150

Common Calculations

PREN (Pitting Resistance) 18
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
190
Resilience: Unit (Modulus of Resilience), kJ/m3 180
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 6.8
4.3
Thermal Shock Resistance, points 19
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 17.5 to 18.5
16.5 to 18.5
Iron (Fe), % 77.8 to 82.1
62.8 to 71.5
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 0
10 to 13
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0.1 to 0.6
0