EN 1.4509 Stainless Steel vs. N08904 Stainless Steel

Both EN 1.4509 stainless steel and N08904 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 65% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is N08904 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
38
Fatigue Strength, MPa 170
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Shear Strength, MPa 330
370
Tensile Strength: Ultimate (UTS), MPa 530
540
Tensile Strength: Yield (Proof), MPa 260
240

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 570
430
Maximum Temperature: Mechanical, °C 890
1100
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
32
Density, g/cm3 7.7
8.1
Embodied Carbon, kg CO2/kg material 2.8
5.8
Embodied Energy, MJ/kg 41
79
Embodied Water, L/kg 120
200

Common Calculations

PREN (Pitting Resistance) 18
37
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
170
Resilience: Unit (Modulus of Resilience), kJ/m3 180
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 6.8
3.1
Thermal Shock Resistance, points 19
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 17.5 to 18.5
19 to 23
Copper (Cu), % 0
1.0 to 2.0
Iron (Fe), % 77.8 to 82.1
38.8 to 53
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
23 to 28
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.035
Titanium (Ti), % 0.1 to 0.6
0