EN 1.4509 Stainless Steel vs. S32615 Stainless Steel

Both EN 1.4509 stainless steel and S32615 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 71% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is S32615 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
28
Fatigue Strength, MPa 170
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Shear Strength, MPa 330
400
Tensile Strength: Ultimate (UTS), MPa 530
620
Tensile Strength: Yield (Proof), MPa 260
250

Thermal Properties

Latent Heat of Fusion, J/g 280
370
Maximum Temperature: Corrosion, °C 570
410
Maximum Temperature: Mechanical, °C 890
990
Melting Completion (Liquidus), °C 1440
1350
Melting Onset (Solidus), °C 1400
1310
Specific Heat Capacity, J/kg-K 480
500
Thermal Expansion, µm/m-K 10
15

Otherwise Unclassified Properties

Base Metal Price, % relative 13
24
Density, g/cm3 7.7
7.6
Embodied Carbon, kg CO2/kg material 2.8
4.4
Embodied Energy, MJ/kg 41
63
Embodied Water, L/kg 120
170

Common Calculations

PREN (Pitting Resistance) 18
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
140
Resilience: Unit (Modulus of Resilience), kJ/m3 180
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 19
21
Thermal Shock Resistance, points 19
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.070
Chromium (Cr), % 17.5 to 18.5
16.5 to 19.5
Copper (Cu), % 0
1.5 to 2.5
Iron (Fe), % 77.8 to 82.1
46.4 to 57.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0
0.3 to 1.5
Nickel (Ni), % 0
19 to 22
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
4.8 to 6.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.1 to 0.6
0