EN 1.4509 Stainless Steel vs. S39277 Stainless Steel

Both EN 1.4509 stainless steel and S39277 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is S39277 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
28
Fatigue Strength, MPa 170
480
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
80
Shear Strength, MPa 330
600
Tensile Strength: Ultimate (UTS), MPa 530
930
Tensile Strength: Yield (Proof), MPa 260
660

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 570
450
Maximum Temperature: Mechanical, °C 890
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
16
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
23
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.8
4.2
Embodied Energy, MJ/kg 41
59
Embodied Water, L/kg 120
180

Common Calculations

PREN (Pitting Resistance) 18
43
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
240
Resilience: Unit (Modulus of Resilience), kJ/m3 180
1070
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
33
Strength to Weight: Bending, points 19
27
Thermal Diffusivity, mm2/s 6.8
4.2
Thermal Shock Resistance, points 19
26

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.025
Chromium (Cr), % 17.5 to 18.5
24 to 26
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 77.8 to 82.1
56.8 to 64.3
Manganese (Mn), % 0 to 1.0
0 to 0.8
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 0
6.5 to 8.0
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0.23 to 0.33
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.0020
Titanium (Ti), % 0.1 to 0.6
0
Tungsten (W), % 0
0.8 to 1.2