EN 1.4509 Stainless Steel vs. S40910 Stainless Steel

Both EN 1.4509 stainless steel and S40910 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4509 stainless steel and the bottom bar is S40910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
160
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
23
Fatigue Strength, MPa 170
130
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Shear Strength, MPa 330
270
Tensile Strength: Ultimate (UTS), MPa 530
430
Tensile Strength: Yield (Proof), MPa 260
190

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Corrosion, °C 570
440
Maximum Temperature: Mechanical, °C 890
710
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
26
Thermal Expansion, µm/m-K 10
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
7.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.8
2.0
Embodied Energy, MJ/kg 41
28
Embodied Water, L/kg 120
94

Common Calculations

PREN (Pitting Resistance) 18
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
80
Resilience: Unit (Modulus of Resilience), kJ/m3 180
94
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 6.8
6.9
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 18.5
10.5 to 11.7
Iron (Fe), % 77.8 to 82.1
85 to 89.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0.3 to 1.0
0 to 0.17
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0.1 to 0.6
0 to 0.5