EN 1.4541 Stainless Steel vs. S30815 Stainless Steel

Both EN 1.4541 stainless steel and S30815 stainless steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4541 stainless steel and the bottom bar is S30815 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 14 to 40
45
Fatigue Strength, MPa 190 to 330
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 410 to 550
480
Tensile Strength: Ultimate (UTS), MPa 600 to 900
680
Tensile Strength: Yield (Proof), MPa 220 to 570
350

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Corrosion, °C 480
430
Maximum Temperature: Mechanical, °C 940
1020
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1380
1360
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 16
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.2
3.3
Embodied Energy, MJ/kg 46
47
Embodied Water, L/kg 140
160

Common Calculations

PREN (Pitting Resistance) 18
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
260
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 830
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 32
25
Strength to Weight: Bending, points 20 to 27
22
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 14 to 20
15

Alloy Composition

Carbon (C), % 0 to 0.080
0.050 to 0.1
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 17 to 19
20 to 22
Iron (Fe), % 65.2 to 74
62.8 to 68.4
Manganese (Mn), % 0 to 2.0
0 to 0.8
Nickel (Ni), % 9.0 to 12
10 to 12
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
1.4 to 2.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.7
0