EN 1.4567 Stainless Steel vs. SAE-AISI 1016 Steel
Both EN 1.4567 stainless steel and SAE-AISI 1016 steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4567 stainless steel and the bottom bar is SAE-AISI 1016 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 240 | |
| 120 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 to 51 | |
| 21 to 28 |
| Fatigue Strength, MPa | 190 to 260 | |
| 180 to 270 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Shear Strength, MPa | 390 to 490 | |
| 280 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 780 | |
| 430 to 480 |
| Tensile Strength: Yield (Proof), MPa | 200 to 390 | |
| 240 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 400 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 52 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 43 | |
| 18 |
| Embodied Water, L/kg | 150 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 220 | |
| 92 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 400 | |
| 150 to 410 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 27 | |
| 15 to 17 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 14 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 13 to 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.040 | |
| 0.13 to 0.18 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Iron (Fe), % | 63.3 to 71.5 | |
| 98.8 to 99.27 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.6 to 0.9 |
| Nickel (Ni), % | 8.5 to 10.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |