EN 1.4571 Stainless Steel vs. R30816 Cobalt

EN 1.4571 stainless steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4571 stainless steel and the bottom bar is R30816 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
280
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 14 to 40
23
Fatigue Strength, MPa 200 to 330
250
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 78
81
Tensile Strength: Ultimate (UTS), MPa 600 to 900
1020
Tensile Strength: Yield (Proof), MPa 230 to 570
460

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Melting Completion (Liquidus), °C 1440
1540
Melting Onset (Solidus), °C 1400
1460
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
9.1
Embodied Carbon, kg CO2/kg material 3.9
20
Embodied Energy, MJ/kg 54
320
Embodied Water, L/kg 150
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
190
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 820
510
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 21 to 32
31
Strength to Weight: Bending, points 20 to 26
25
Thermal Diffusivity, mm2/s 4.0
3.3
Thermal Shock Resistance, points 13 to 20
28

Alloy Composition

Carbon (C), % 0 to 0.080
0.32 to 0.42
Chromium (Cr), % 16.5 to 18.5
19 to 21
Cobalt (Co), % 0
40 to 49.8
Iron (Fe), % 61.7 to 71
0 to 5.0
Manganese (Mn), % 0 to 2.0
1.0 to 2.0
Molybdenum (Mo), % 2.0 to 2.5
3.5 to 4.5
Nickel (Ni), % 10.5 to 13.5
19 to 21
Niobium (Nb), % 0
3.5 to 4.5
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Tantalum (Ta), % 0
3.5 to 4.5
Titanium (Ti), % 0 to 0.7
0
Tungsten (W), % 0
3.5 to 4.5