EN 1.4587 Stainless Steel vs. AISI 302B Stainless Steel

Both EN 1.4587 stainless steel and AISI 302B stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is AISI 302B stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
45
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 540
580
Tensile Strength: Yield (Proof), MPa 250
230

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
930
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1370
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 17
17
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 36
15
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
3.0
Embodied Energy, MJ/kg 87
43
Embodied Water, L/kg 230
140

Common Calculations

PREN (Pitting Resistance) 43
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
210
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
21
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.5
4.4
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 24 to 26
17 to 19
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
65.7 to 73
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
8.0 to 10
Nitrogen (N), % 0.15 to 0.25
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
2.0 to 3.0
Sulfur (S), % 0 to 0.025
0 to 0.030