EN 1.4587 Stainless Steel vs. AISI 316L Stainless Steel

Both EN 1.4587 stainless steel and AISI 316L stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is AISI 316L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170 to 350
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
9.0 to 50
Fatigue Strength, MPa 200
170 to 450
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 540
530 to 1160
Tensile Strength: Yield (Proof), MPa 250
190 to 870

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 36
19
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.3
3.9
Embodied Energy, MJ/kg 87
53
Embodied Water, L/kg 230
150

Common Calculations

PREN (Pitting Resistance) 43
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
77 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 150
93 to 1880
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
19 to 41
Strength to Weight: Bending, points 18
18 to 31
Thermal Diffusivity, mm2/s 4.5
4.1
Thermal Shock Resistance, points 13
12 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
16 to 18
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
62 to 72
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
2.0 to 3.0
Nickel (Ni), % 28 to 30
10 to 14
Nitrogen (N), % 0.15 to 0.25
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.025
0 to 0.030