EN 1.4587 stainless steel belongs to the iron alloys classification, while AWS BAg-19 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is AWS BAg-19.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
74
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 80
27
Tensile Strength: Ultimate (UTS), MPa 540
140

Thermal Properties

Latent Heat of Fusion, J/g 310
120
Melting Completion (Liquidus), °C 1420
890
Melting Onset (Solidus), °C 1370
760
Specific Heat Capacity, J/kg-K 470
250
Thermal Expansion, µm/m-K 15
20

Otherwise Unclassified Properties

Density, g/cm3 8.1
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.0
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 18
3.8
Strength to Weight: Bending, points 18
5.8
Thermal Shock Resistance, points 13
6.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
6.6 to 7.9
Iron (Fe), % 32.7 to 41.9
0
Lithium (Li), % 0
0.15 to 0.3
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
92 to 93
Sulfur (S), % 0 to 0.025
0
Residuals, % 0
0 to 0.15