EN 1.4587 Stainless Steel vs. AWS BVAg-8

EN 1.4587 stainless steel belongs to the iron alloys classification, while AWS BVAg-8 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is AWS BVAg-8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
84
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 80
31
Tensile Strength: Ultimate (UTS), MPa 540
170

Thermal Properties

Latent Heat of Fusion, J/g 310
140
Melting Completion (Liquidus), °C 1420
780
Melting Onset (Solidus), °C 1370
780
Specific Heat Capacity, J/kg-K 470
280
Thermal Expansion, µm/m-K 15
19

Otherwise Unclassified Properties

Density, g/cm3 8.1
10

Common Calculations

Stiffness to Weight: Axial, points 14
4.6
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 18
4.7
Strength to Weight: Bending, points 18
6.8
Thermal Shock Resistance, points 13
7.6

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.030
0 to 0.0050
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
27 to 29
Iron (Fe), % 32.7 to 41.9
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.0020
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
71 to 73
Sulfur (S), % 0 to 0.025
0
Zinc (Zn), % 0
0 to 0.0010