EN 1.4587 Stainless Steel vs. AWS E219

Both EN 1.4587 stainless steel and AWS E219 are iron alloys. They have 66% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is AWS E219.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
17
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 540
690

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1370
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 17
14
Thermal Expansion, µm/m-K 15
15

Otherwise Unclassified Properties

Base Metal Price, % relative 36
15
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
3.1
Embodied Energy, MJ/kg 87
44
Embodied Water, L/kg 230
160

Common Calculations

PREN (Pitting Resistance) 43
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
25
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 4.5
3.8
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 24 to 26
19 to 21.5
Copper (Cu), % 2.0 to 3.0
0 to 0.75
Iron (Fe), % 32.7 to 41.9
58.6 to 67.4
Manganese (Mn), % 0 to 2.0
8.0 to 10
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.75
Nickel (Ni), % 28 to 30
5.5 to 7.0
Nitrogen (N), % 0.15 to 0.25
0.1 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030