EN 1.4587 Stainless Steel vs. Commercially Pure Palladium

EN 1.4587 stainless steel belongs to the iron alloys classification, while commercially pure palladium belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is commercially pure palladium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
1.1 to 11
Poisson's Ratio 0.28
0.39
Shear Modulus, GPa 80
43
Tensile Strength: Ultimate (UTS), MPa 540
200 to 380

Thermal Properties

Latent Heat of Fusion, J/g 310
160
Melting Completion (Liquidus), °C 1420
1550
Melting Onset (Solidus), °C 1370
1550
Specific Heat Capacity, J/kg-K 470
240
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
16
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
12

Otherwise Unclassified Properties

Density, g/cm3 8.1
12

Common Calculations

Stiffness to Weight: Axial, points 14
5.6
Stiffness to Weight: Bending, points 24
14
Strength to Weight: Axial, points 18
4.5 to 8.8
Strength to Weight: Bending, points 18
6.2 to 9.7
Thermal Shock Resistance, points 13
9.8 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
0
Nitrogen (N), % 0.15 to 0.25
0
Palladium (Pd), % 0
99.8 to 100
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.025
0
Residuals, % 0
0 to 0.2