EN 1.4587 Stainless Steel vs. EN 1.4807 Stainless Steel

Both EN 1.4587 stainless steel and EN 1.4807 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is EN 1.4807 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
4.5
Fatigue Strength, MPa 200
120
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 540
480
Tensile Strength: Yield (Proof), MPa 250
250

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 450
600
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1420
1390
Melting Onset (Solidus), °C 1370
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 15
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 36
39
Density, g/cm3 8.1
8.0
Embodied Carbon, kg CO2/kg material 6.3
6.8
Embodied Energy, MJ/kg 87
97
Embodied Water, L/kg 230
190

Common Calculations

PREN (Pitting Resistance) 43
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
18
Resilience: Unit (Modulus of Resilience), kJ/m3 150
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
17
Strength to Weight: Bending, points 18
17
Thermal Diffusivity, mm2/s 4.5
3.2
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.5
Chromium (Cr), % 24 to 26
17 to 20
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
36.6 to 46.7
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.5
Nickel (Ni), % 28 to 30
34 to 36
Niobium (Nb), % 0
1.0 to 1.8
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.025
0 to 0.030