EN 1.4587 Stainless Steel vs. SAE-AISI O2 Steel

Both EN 1.4587 stainless steel and SAE-AISI O2 steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is SAE-AISI O2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Tensile Strength: Ultimate (UTS), MPa 540
640 to 2050

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
43
Thermal Expansion, µm/m-K 15
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.4
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
1.8
Embodied Energy, MJ/kg 87
26
Embodied Water, L/kg 230
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
23 to 73
Strength to Weight: Bending, points 18
21 to 46
Thermal Diffusivity, mm2/s 4.5
12
Thermal Shock Resistance, points 13
22 to 70

Alloy Composition

Carbon (C), % 0 to 0.030
0.85 to 1.0
Chromium (Cr), % 24 to 26
0 to 0.5
Copper (Cu), % 2.0 to 3.0
0 to 0.25
Iron (Fe), % 32.7 to 41.9
95 to 97.8
Manganese (Mn), % 0 to 2.0
1.4 to 1.8
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.3
Nickel (Ni), % 28 to 30
0 to 0.3
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0
0 to 0.3