EN 1.4587 Stainless Steel vs. C11300 Copper

EN 1.4587 stainless steel belongs to the iron alloys classification, while C11300 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is C11300 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
2.3 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 80
43
Tensile Strength: Ultimate (UTS), MPa 540
230 to 410
Tensile Strength: Yield (Proof), MPa 250
77 to 400

Thermal Properties

Latent Heat of Fusion, J/g 310
210
Maximum Temperature: Mechanical, °C 1100
200
Melting Completion (Liquidus), °C 1420
1080
Melting Onset (Solidus), °C 1370
1030
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 17
390
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
100
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
100

Otherwise Unclassified Properties

Base Metal Price, % relative 36
32
Density, g/cm3 8.1
9.0
Embodied Carbon, kg CO2/kg material 6.3
2.6
Embodied Energy, MJ/kg 87
42
Embodied Water, L/kg 230
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
8.5 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 150
25 to 690
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 18
7.2 to 13
Strength to Weight: Bending, points 18
9.4 to 14
Thermal Diffusivity, mm2/s 4.5
110
Thermal Shock Resistance, points 13
8.2 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
99.85 to 99.973
Iron (Fe), % 32.7 to 41.9
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0.027 to 0.050
Sulfur (S), % 0 to 0.025
0
Residuals, % 0
0 to 0.1