EN 1.4587 Stainless Steel vs. C12000 Copper

EN 1.4587 stainless steel belongs to the iron alloys classification, while C12000 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is C12000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
2.8 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 80
43
Tensile Strength: Ultimate (UTS), MPa 540
230 to 410
Tensile Strength: Yield (Proof), MPa 250
77 to 400

Thermal Properties

Latent Heat of Fusion, J/g 310
210
Maximum Temperature: Mechanical, °C 1100
200
Melting Completion (Liquidus), °C 1420
1080
Melting Onset (Solidus), °C 1370
1080
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 17
390
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
98
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
98

Otherwise Unclassified Properties

Base Metal Price, % relative 36
31
Density, g/cm3 8.1
9.0
Embodied Carbon, kg CO2/kg material 6.3
2.6
Embodied Energy, MJ/kg 87
41
Embodied Water, L/kg 230
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
10 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 150
25 to 690
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 18
7.2 to 13
Strength to Weight: Bending, points 18
9.4 to 14
Thermal Diffusivity, mm2/s 4.5
110
Thermal Shock Resistance, points 13
8.2 to 15

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
99.9 to 99.996
Iron (Fe), % 32.7 to 41.9
0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0.0040 to 0.012
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.025
0