EN 1.4587 Stainless Steel vs. C97300 Nickel Silver

EN 1.4587 stainless steel belongs to the iron alloys classification, while C97300 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is C97300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
9.0
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 80
40
Tensile Strength: Ultimate (UTS), MPa 540
230
Tensile Strength: Yield (Proof), MPa 250
110

Thermal Properties

Latent Heat of Fusion, J/g 310
180
Maximum Temperature: Mechanical, °C 1100
150
Melting Completion (Liquidus), °C 1420
1040
Melting Onset (Solidus), °C 1370
1010
Specific Heat Capacity, J/kg-K 470
370
Thermal Conductivity, W/m-K 17
29
Thermal Expansion, µm/m-K 15
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 36
30
Density, g/cm3 8.1
8.6
Embodied Carbon, kg CO2/kg material 6.3
3.7
Embodied Energy, MJ/kg 87
59
Embodied Water, L/kg 230
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
18
Resilience: Unit (Modulus of Resilience), kJ/m3 150
59
Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 18
7.6
Strength to Weight: Bending, points 18
9.8
Thermal Diffusivity, mm2/s 4.5
9.3
Thermal Shock Resistance, points 13
8.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.35
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 2.0 to 3.0
53 to 58
Iron (Fe), % 32.7 to 41.9
0 to 1.5
Lead (Pb), % 0
8.0 to 11
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 28 to 30
11 to 14
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.050
Silicon (Si), % 0 to 1.0
0 to 0.15
Sulfur (S), % 0 to 0.025
0 to 0.080
Tin (Sn), % 0
1.5 to 3.0
Zinc (Zn), % 0
17 to 25
Residuals, % 0
0 to 1.0