EN 1.4587 Stainless Steel vs. N08028 Stainless Steel

Both EN 1.4587 stainless steel and N08028 stainless steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is N08028 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
45
Fatigue Strength, MPa 200
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 540
570
Tensile Strength: Yield (Proof), MPa 250
240

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 450
460
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 17
12
Thermal Expansion, µm/m-K 15
16

Otherwise Unclassified Properties

Base Metal Price, % relative 36
37
Density, g/cm3 8.1
8.1
Embodied Carbon, kg CO2/kg material 6.3
6.4
Embodied Energy, MJ/kg 87
89
Embodied Water, L/kg 230
240

Common Calculations

PREN (Pitting Resistance) 43
39
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
210
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.5
3.2
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
26 to 28
Copper (Cu), % 2.0 to 3.0
0.6 to 1.4
Iron (Fe), % 32.7 to 41.9
29 to 40.4
Manganese (Mn), % 0 to 2.0
0 to 2.5
Molybdenum (Mo), % 4.0 to 5.0
3.0 to 4.0
Nickel (Ni), % 28 to 30
30 to 34
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030