EN 1.4587 Stainless Steel vs. N08366 Stainless Steel

Both EN 1.4587 stainless steel and N08366 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is N08366 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
180
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
34
Fatigue Strength, MPa 200
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 250
240

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 450
430
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 36
33
Density, g/cm3 8.1
8.1
Embodied Carbon, kg CO2/kg material 6.3
6.2
Embodied Energy, MJ/kg 87
84
Embodied Water, L/kg 230
200

Common Calculations

PREN (Pitting Resistance) 43
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
160
Resilience: Unit (Modulus of Resilience), kJ/m3 150
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.5
3.4
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.035
Chromium (Cr), % 24 to 26
20 to 22
Copper (Cu), % 2.0 to 3.0
0
Iron (Fe), % 32.7 to 41.9
42.4 to 50.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
6.0 to 7.0
Nickel (Ni), % 28 to 30
23.5 to 25.5
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030