EN 1.4587 Stainless Steel vs. S32906 Stainless Steel

Both EN 1.4587 stainless steel and S32906 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4587 stainless steel and the bottom bar is S32906 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
270
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
28
Fatigue Strength, MPa 200
460
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 540
850
Tensile Strength: Yield (Proof), MPa 250
620

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 450
460
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 17
13
Thermal Expansion, µm/m-K 15
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 36
20
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
3.7
Embodied Energy, MJ/kg 87
52
Embodied Water, L/kg 230
190

Common Calculations

PREN (Pitting Resistance) 43
41
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
220
Resilience: Unit (Modulus of Resilience), kJ/m3 150
950
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
30
Strength to Weight: Bending, points 18
26
Thermal Diffusivity, mm2/s 4.5
3.6
Thermal Shock Resistance, points 13
23

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 24 to 26
28 to 30
Copper (Cu), % 2.0 to 3.0
0 to 0.8
Iron (Fe), % 32.7 to 41.9
56.6 to 63.6
Manganese (Mn), % 0 to 2.0
0.8 to 1.5
Molybdenum (Mo), % 4.0 to 5.0
1.5 to 2.6
Nickel (Ni), % 28 to 30
5.8 to 7.5
Nitrogen (N), % 0.15 to 0.25
0.3 to 0.4
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.025
0 to 0.030