EN 1.4611 Stainless Steel vs. SAE-AISI 4140 Steel

Both EN 1.4611 stainless steel and SAE-AISI 4140 steel are iron alloys. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4611 stainless steel and the bottom bar is SAE-AISI 4140 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200 to 310
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
11 to 26
Fatigue Strength, MPa 180
360 to 650
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 330
410 to 660
Tensile Strength: Ultimate (UTS), MPa 530
690 to 1080
Tensile Strength: Yield (Proof), MPa 280
590 to 990

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 970
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
43
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.4
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.5
Embodied Energy, MJ/kg 36
20
Embodied Water, L/kg 140
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
74 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 190
920 to 2590
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
25 to 38
Strength to Weight: Bending, points 19
22 to 30
Thermal Diffusivity, mm2/s 5.7
12
Thermal Shock Resistance, points 18
20 to 32

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0 to 0.030
0.38 to 0.43
Chromium (Cr), % 19 to 22
0.8 to 1.1
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 73.3 to 80.8
96.8 to 97.8
Manganese (Mn), % 0 to 1.0
0.75 to 1.0
Molybdenum (Mo), % 0 to 0.5
0.15 to 0.25
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.050
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.050
0 to 0.040
Titanium (Ti), % 0.2 to 1.0
0