EN 1.4634 Stainless Steel vs. ACI-ASTM CG6MMN Steel

Both EN 1.4634 stainless steel and ACI-ASTM CG6MMN steel are iron alloys. They have 77% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is ACI-ASTM CG6MMN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
34
Fatigue Strength, MPa 180
260
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 540
670
Tensile Strength: Yield (Proof), MPa 280
320

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 500
460
Maximum Temperature: Mechanical, °C 900
1080
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
17

Otherwise Unclassified Properties

Base Metal Price, % relative 13
22
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
4.8
Embodied Energy, MJ/kg 42
68
Embodied Water, L/kg 140
180

Common Calculations

PREN (Pitting Resistance) 19
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
190
Resilience: Unit (Modulus of Resilience), kJ/m3 200
260
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 19
14

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.060
Chromium (Cr), % 17.5 to 18.5
20.5 to 23.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
51.9 to 62.1
Manganese (Mn), % 0 to 1.0
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.5
1.5 to 3.0
Nickel (Ni), % 0 to 0.5
11.5 to 13.5
Niobium (Nb), % 0.3 to 1.0
0.1 to 0.3
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Vanadium (V), % 0
0.1 to 0.3