MakeItFrom.com
Menu (ESC)

EN 1.4634 Stainless Steel vs. AISI 204 Stainless Steel

Both EN 1.4634 stainless steel and AISI 204 stainless steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is AISI 204 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
23 to 39
Fatigue Strength, MPa 180
320 to 720
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 340
500 to 700
Tensile Strength: Ultimate (UTS), MPa 540
730 to 1100
Tensile Strength: Yield (Proof), MPa 280
380 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 500
410
Maximum Temperature: Mechanical, °C 900
850
Melting Completion (Liquidus), °C 1430
1410
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
10
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.9
2.4
Embodied Energy, MJ/kg 42
35
Embodied Water, L/kg 140
130

Common Calculations

PREN (Pitting Resistance) 19
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
240 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 200
360 to 2940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
27 to 40
Strength to Weight: Bending, points 19
24 to 31
Thermal Diffusivity, mm2/s 5.8
4.1
Thermal Shock Resistance, points 19
16 to 24

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 18.5
15 to 17
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
69.6 to 76.4
Manganese (Mn), % 0 to 1.0
7.0 to 9.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
1.5 to 3.0
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030