EN 1.4634 Stainless Steel vs. ASTM A182 Grade F11 Class 1

Both EN 1.4634 stainless steel and ASTM A182 grade F11 class 1 are iron alloys. Both are furnished in the annealed condition. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is ASTM A182 grade F11 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
23
Fatigue Strength, MPa 180
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 340
300
Tensile Strength: Ultimate (UTS), MPa 540
470
Tensile Strength: Yield (Proof), MPa 280
230

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 900
430
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
39
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.6
Embodied Energy, MJ/kg 42
21
Embodied Water, L/kg 140
52

Common Calculations

PREN (Pitting Resistance) 19
3.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
89
Resilience: Unit (Modulus of Resilience), kJ/m3 200
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 5.8
11
Thermal Shock Resistance, points 19
14

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0.050 to 0.15
Chromium (Cr), % 17.5 to 18.5
1.0 to 1.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
96 to 97.7
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.5
0.44 to 0.65
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.030
Silicon (Si), % 0.2 to 1.5
0.5 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030