EN 1.4634 Stainless Steel vs. ASTM A588 Steel

Both EN 1.4634 stainless steel and ASTM A588 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is ASTM A588 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
22
Fatigue Strength, MPa 180
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 340
350
Tensile Strength: Ultimate (UTS), MPa 540
550
Tensile Strength: Yield (Proof), MPa 280
390

Thermal Properties

Latent Heat of Fusion, J/g 290
250 to 260
Maximum Temperature: Mechanical, °C 900
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410 to 1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
43 to 44
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3 to 2.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.5 to 1.6
Embodied Energy, MJ/kg 42
20 to 22
Embodied Water, L/kg 140
50 to 51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
110
Resilience: Unit (Modulus of Resilience), kJ/m3 200
400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 5.8
12
Thermal Shock Resistance, points 19
16