EN 1.4634 Stainless Steel vs. EN 1.4373 Stainless Steel

Both EN 1.4634 stainless steel and EN 1.4373 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is EN 1.4373 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
46
Fatigue Strength, MPa 180
340
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 340
530
Tensile Strength: Ultimate (UTS), MPa 540
750
Tensile Strength: Yield (Proof), MPa 280
370

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 500
410
Maximum Temperature: Mechanical, °C 900
910
Melting Completion (Liquidus), °C 1430
1400
Melting Onset (Solidus), °C 1390
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 13
13
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.9
2.8
Embodied Energy, MJ/kg 42
40
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 19
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
290
Resilience: Unit (Modulus of Resilience), kJ/m3 200
340
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 5.8
4.0
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 17.5 to 18.5
17 to 19
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
63 to 71.5
Manganese (Mn), % 0 to 1.0
7.5 to 10.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
4.0 to 6.0
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0.050 to 0.25
Phosphorus (P), % 0 to 0.050
0 to 0.045
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.015