EN 1.4634 Stainless Steel vs. EN 1.4941 Stainless Steel

Both EN 1.4634 stainless steel and EN 1.4941 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is EN 1.4941 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
39
Fatigue Strength, MPa 180
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 340
400
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 280
210

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 500
520
Maximum Temperature: Mechanical, °C 900
940
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
16
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 13
16
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
3.3
Embodied Energy, MJ/kg 42
47
Embodied Water, L/kg 140
140

Common Calculations

PREN (Pitting Resistance) 19
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
180
Resilience: Unit (Modulus of Resilience), kJ/m3 200
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 5.8
4.3
Thermal Shock Resistance, points 19
13

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 17.5 to 18.5
17 to 19
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
65.1 to 73.6
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
9.0 to 12
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.035
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.015
Titanium (Ti), % 0
0.4 to 0.8