EN 1.4634 Stainless Steel vs. EN 1.6781 Steel

Both EN 1.4634 stainless steel and EN 1.6781 steel are iron alloys. They have 81% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is EN 1.6781 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
17
Fatigue Strength, MPa 180
450
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 540
830
Tensile Strength: Yield (Proof), MPa 280
680

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 900
450
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
44
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 13
5.0
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.9
1.9
Embodied Energy, MJ/kg 42
25
Embodied Water, L/kg 140
60

Common Calculations

PREN (Pitting Resistance) 19
3.3
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
130
Resilience: Unit (Modulus of Resilience), kJ/m3 200
1220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
29
Strength to Weight: Bending, points 19
25
Thermal Diffusivity, mm2/s 5.8
12
Thermal Shock Resistance, points 19
24

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0.15 to 0.19
Chromium (Cr), % 17.5 to 18.5
1.3 to 1.8
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
92.6 to 94.6
Manganese (Mn), % 0 to 1.0
0.55 to 0.8
Molybdenum (Mo), % 0 to 0.5
0.45 to 0.6
Nickel (Ni), % 0 to 0.5
3.0 to 3.5
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.015
Silicon (Si), % 0.2 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.015