EN 1.4634 Stainless Steel vs. EN 1.7376 Steel

Both EN 1.4634 stainless steel and EN 1.7376 steel are iron alloys. They have 89% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is EN 1.7376 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
20
Fatigue Strength, MPa 180
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 540
710
Tensile Strength: Yield (Proof), MPa 280
460

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Mechanical, °C 900
600
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
26
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
11

Otherwise Unclassified Properties

Base Metal Price, % relative 13
6.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
2.1
Embodied Energy, MJ/kg 42
29
Embodied Water, L/kg 140
88

Common Calculations

PREN (Pitting Resistance) 19
12
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
130
Resilience: Unit (Modulus of Resilience), kJ/m3 200
560
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 5.8
6.9
Thermal Shock Resistance, points 19
20

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0.12 to 0.19
Chromium (Cr), % 17.5 to 18.5
8.0 to 10
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 74.9 to 81.8
86.2 to 90.6
Manganese (Mn), % 0 to 1.0
0.35 to 0.65
Molybdenum (Mo), % 0 to 0.5
0.9 to 1.2
Nickel (Ni), % 0 to 0.5
0 to 0.4
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.030
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030
Vanadium (V), % 0
0 to 0.050