EN 1.4634 Stainless Steel vs. SAE-AISI 1213 Steel

Both EN 1.4634 stainless steel and SAE-AISI 1213 steel are iron alloys. They have 79% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is SAE-AISI 1213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
11 to 29
Fatigue Strength, MPa 180
200 to 290
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 340
290 to 360
Tensile Strength: Ultimate (UTS), MPa 540
440 to 600
Tensile Strength: Yield (Proof), MPa 280
260 to 470

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 900
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.4
Embodied Energy, MJ/kg 42
18
Embodied Water, L/kg 140
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
63 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 200
180 to 580
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
16 to 21
Strength to Weight: Bending, points 19
17 to 20
Thermal Diffusivity, mm2/s 5.8
14
Thermal Shock Resistance, points 19
14 to 19

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.13
Chromium (Cr), % 17.5 to 18.5
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
98.4 to 99
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0.070 to 0.12
Silicon (Si), % 0.2 to 1.5
0
Sulfur (S), % 0 to 0.050
0.24 to 0.33