EN 1.4634 Stainless Steel vs. S30435 Stainless Steel

Both EN 1.4634 stainless steel and S30435 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is S30435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 21
51
Fatigue Strength, MPa 180
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Shear Strength, MPa 340
370
Tensile Strength: Ultimate (UTS), MPa 540
510
Tensile Strength: Yield (Proof), MPa 280
170

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 500
410
Maximum Temperature: Mechanical, °C 900
900
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
16
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 13
14
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
2.9
Embodied Energy, MJ/kg 42
40
Embodied Water, L/kg 140
140

Common Calculations

PREN (Pitting Resistance) 19
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
210
Resilience: Unit (Modulus of Resilience), kJ/m3 200
77
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
18
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 5.8
4.2
Thermal Shock Resistance, points 19
12

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 17.5 to 18.5
16 to 18
Copper (Cu), % 0 to 0.5
1.5 to 3.0
Iron (Fe), % 74.9 to 81.8
66.9 to 75.5
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
7.0 to 9.0
Niobium (Nb), % 0.3 to 1.0
0
Phosphorus (P), % 0 to 0.050
0 to 0.045
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030