EN 1.4634 Stainless Steel vs. S32003 Stainless Steel

Both EN 1.4634 stainless steel and S32003 stainless steel are iron alloys. Both are furnished in the annealed condition. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is S32003 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
28
Fatigue Strength, MPa 180
370
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
79
Shear Strength, MPa 340
480
Tensile Strength: Ultimate (UTS), MPa 540
730
Tensile Strength: Yield (Proof), MPa 280
510

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 500
430
Maximum Temperature: Mechanical, °C 900
1010
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 13
14
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
3.0
Embodied Energy, MJ/kg 42
42
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 19
29
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
180
Resilience: Unit (Modulus of Resilience), kJ/m3 200
660
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 5.8
4.0
Thermal Shock Resistance, points 19
21

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17.5 to 18.5
19.5 to 22.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
68.2 to 75.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
1.5 to 2.0
Nickel (Ni), % 0 to 0.5
3.0 to 4.0
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.050
0 to 0.030
Silicon (Si), % 0.2 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.020