EN 1.4634 Stainless Steel vs. S35315 Stainless Steel

Both EN 1.4634 stainless steel and S35315 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 57% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is S35315 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 21
46
Fatigue Strength, MPa 180
280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 340
520
Tensile Strength: Ultimate (UTS), MPa 540
740
Tensile Strength: Yield (Proof), MPa 280
300

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Maximum Temperature: Corrosion, °C 500
450
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1430
1370
Melting Onset (Solidus), °C 1390
1330
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 13
34
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.9
5.7
Embodied Energy, MJ/kg 42
81
Embodied Water, L/kg 140
220

Common Calculations

PREN (Pitting Resistance) 19
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
270
Resilience: Unit (Modulus of Resilience), kJ/m3 200
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 5.8
3.1
Thermal Shock Resistance, points 19
17

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0.040 to 0.080
Cerium (Ce), % 0
0.030 to 0.1
Chromium (Cr), % 17.5 to 18.5
24 to 26
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 74.9 to 81.8
33.6 to 40.6
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 0.5
34 to 36
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0.12 to 0.18
Phosphorus (P), % 0 to 0.050
0 to 0.040
Silicon (Si), % 0.2 to 1.5
1.2 to 2.0
Sulfur (S), % 0 to 0.050
0 to 0.030