EN 1.4634 Stainless Steel vs. S44800 Stainless Steel

Both EN 1.4634 stainless steel and S44800 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4634 stainless steel and the bottom bar is S44800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 21
23
Fatigue Strength, MPa 180
300
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
82
Shear Strength, MPa 340
370
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 280
450

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 500
460
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
17
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 13
19
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.9
3.8
Embodied Energy, MJ/kg 42
52
Embodied Water, L/kg 140
190

Common Calculations

PREN (Pitting Resistance) 19
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
120
Resilience: Unit (Modulus of Resilience), kJ/m3 200
480
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 5.8
4.6
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0.2 to 1.5
0
Carbon (C), % 0 to 0.030
0 to 0.010
Chromium (Cr), % 17.5 to 18.5
28 to 30
Copper (Cu), % 0 to 0.5
0 to 0.15
Iron (Fe), % 74.9 to 81.8
62.6 to 66.5
Manganese (Mn), % 0 to 1.0
0 to 0.3
Molybdenum (Mo), % 0 to 0.5
3.5 to 4.2
Nickel (Ni), % 0 to 0.5
2.0 to 2.5
Niobium (Nb), % 0.3 to 1.0
0
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.050
0 to 0.025
Silicon (Si), % 0.2 to 1.5
0 to 0.2
Sulfur (S), % 0 to 0.050
0 to 0.020