EN 1.4640 Stainless Steel vs. AWS E309Mo

Both EN 1.4640 stainless steel and AWS E309Mo are iron alloys. They have 85% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4640 stainless steel and the bottom bar is AWS E309Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 51
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 620 to 650
620

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1380
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 14
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.8
4.2
Embodied Energy, MJ/kg 40
59
Embodied Water, L/kg 150
180

Common Calculations

PREN (Pitting Resistance) 20
32
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 23
22
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 4.0
3.9
Thermal Shock Resistance, points 14 to 15
15

Alloy Composition

Carbon (C), % 0.030 to 0.080
0 to 0.12
Chromium (Cr), % 18 to 19
22 to 25
Copper (Cu), % 1.3 to 2.0
0 to 0.75
Iron (Fe), % 67.4 to 73.6
53.6 to 63.5
Manganese (Mn), % 1.5 to 4.0
0.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 5.5 to 6.9
12 to 14
Nitrogen (N), % 0.030 to 0.11
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030